Surface analysis of AISI 410 stainless steel cladding with AlN, Si, Co, and W powders

Tzung-Ming Chen, Hsin Min Lee

研究成果: Article

1 引文 斯高帕斯(Scopus)

摘要

In this study, the surface modiication of AISI 410 stainless steel with an AlN clad layer was investigated. For the purpose of improving the uniformity and combining ability of the clad layer, speciic amounts of elemental Si, W, and Co were added. The gas tungsten arc welding method was used for the cladding procedure. The analysis was focused on the success of the cladding procedure and the modiication efect of the clad layer. To meet the demand mentioned, electron probe microanalysis was used to detect the chemical composition, and scanning electron microscopy was used to observe surface wear. Furthermore, hardness and wear tests were used to verify the mechanical properties, and temperature measurement was used to ensure the heat dissipation. The experimental results show that the surface hardness, wear resistance, and heat dissipation of cladding AISI 410 were better than naked AISI 410.

原文English
頁(從 - 到)1005-1011
頁數7
期刊Sensors and Materials
28
發行號9
DOIs
出版狀態Published - 2016 一月 1

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Instrumentation

指紋 深入研究「Surface analysis of AISI 410 stainless steel cladding with AlN, Si, Co, and W powders」主題。共同形成了獨特的指紋。

  • 引用此