Power factor improvement in hydrothermally synthesized Bi 2-xSb xTe 3 (x=1.5) - Carbon spheree composites

Chia Jyi Liu, Gao Jhih Liu, Chi Jung Su

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

We report fabrication of compacted Bi 0.5Sb 1.5Te 3 composites by adding 1 wt% of carbon spheres in the hydrothermal synthesis. The processing parameter of sintering temperature is investigated in order to optimize the thermoelectric power factor of pressed Bi 0.5Sb 1.5Te 3 composites. As a result, we find that the composite sintered at 360 °C shows the best power factor performance among the composites and has a largest power factor of 15.4 μW/cm K 2 at 205 K and 13.5 μW/cm K 2 at 290 K. When compared with the samples without addition of carbon sphere in the hydrothermal synthesis, the composites sintered at 340 °C and 360 °C both surpass the largest power factor of 12.1 μW/cm K 2 at 280 K and 11.9 μW/cm K 2 at 290 K for the 340 °C-sintered counterpart.

原文English
頁(從 - 到)127-132
頁數6
期刊Journal of Solid State Chemistry
193
DOIs
出版狀態Published - 2012 九月 1

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Inorganic Chemistry
  • Materials Chemistry

指紋 深入研究「Power factor improvement in hydrothermally synthesized Bi <sub>2-x</sub>Sb <sub>x</sub>Te <sub>3</sub> (x=1.5) - Carbon spheree composites」主題。共同形成了獨特的指紋。

引用此