Optical Properties of Indium Doeped ZnO Nanowires

Tsung Shine Ko, Sin Liang Ou, Kuo Sheng Kao, Tz Min Yang, Der Yuh Lin

研究成果: Article

2 引文 斯高帕斯(Scopus)

摘要

We report the synthesis of the ZnO nanowires (NWs) with different indium concentrations by using the thermal evaporation method. The gold nanoparticles were used as the catalyst and were dispersed on the silicon wafer to facilitate the growth of the ZnO NWs. High resolution transmission electron microscopy confirms that the ZnO NWs growth relied on vapor-liquid-solid mechanism and energy dispersion spectrum detects the atomic percentages of indium in ZnO NWs. Scanning electron microscopy shows that the diameters of pure ZnO NWs range from 20 to 30 nm and the diameters of ZnO:In were increased to 50-80 nm with increasing indium doping level. X-ray diffraction results point out that the crystal quality of the ZnO NWs was worse with doping higher indium concentration. Photoluminescence (PL) study of the ZnO NWs exhibited main photoemission at 380 nm due to the recombination of excitons in near-band-edge (NBE). In addition, PL results also indicate the slightly blue shift and PL intensity decreasing of NBE emission from the ZnO NWs with higher indium concentrations could be attributed to more donor-induced trap center generations.

原文English
文章編號760376
期刊International Journal of Photoenergy
2015
DOIs
出版狀態Published - 2015

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Atomic and Molecular Physics, and Optics
  • Renewable Energy, Sustainability and the Environment
  • Materials Science(all)

指紋 深入研究「Optical Properties of Indium Doeped ZnO Nanowires」主題。共同形成了獨特的指紋。

  • 引用此