Observation of multiple transitions on permalloy ring by magnetic force microscopy

L. K. Lin, C. Y. Kuo, J. Y. Ou, C. C. Chang, C. R. Chang, Lance Horng, J. C. Wu

研究成果: Conference article同行評審

2 引文 斯高帕斯(Scopus)

摘要

We present a study of magnetization reversal on microstructured permalloy thin film rings using a magnetic force microscopy in the presence of external magnetic fields up to 540 Oe. Permalloy rings with fixed thickness/outside diameter of 23 nm/5 μm and inside diameter of 2.2 and 2.6μm, respectively, were fabricated by using standard electron beam lithography through a lift-off process. Four transitions during magnetization reversal were observed on the one with 2.2 μm inside diameter, in which the magnetization was evolved from onion to vortex-pair, vortex-pair to vortex, vortex to vortex-core, vortex-core to reverse onion state. The remanent state was flux closure vortex state. A similar magnetization evolution occurred on the one with 2.6 μm inside diameter except that the remanent state was vortex pair. The numerical simulation results using OOMMF showed good agreement with the experimental results. These multiple stable states during the magnetization reversal may provide an excellent opportunity for developing multibit storage cells.

原文English
頁(從 - 到)4360-4363
頁數4
期刊Physica Status Solidi (C) Current Topics in Solid State Physics
4
發行號12
DOIs
出版狀態Published - 2007 十二月 1
事件International Symposium on Advanced Magnetic Materials and Appilications, (ISAMMA 2007) - Jeju, Korea, Republic of
持續時間: 2007 五月 282007 六月 1

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics

指紋 深入研究「Observation of multiple transitions on permalloy ring by magnetic force microscopy」主題。共同形成了獨特的指紋。

引用此