Microwave-assisted rapid fabrication of Co3O4 nanorods and application to the degradation of phenol

Teh Long Lai, Yuan Lung Lai, Chia Chan Lee, Youn Yuen Shu, Chen Bin Wang

研究成果: Article

96 引文 斯高帕斯(Scopus)

摘要

A novel microwave-assisted hydrothermal route for preparation of Co3O4 nanorods had been developed. The process contained two steps: first, nanorods of cobalt hydroxide carbonate were obtained from a mixed solution of 50 ml of 0.6 M Co(NO3)2·6H2O and 2.4 g of urea under 500 W microwave irradiated for 3 min. Then, the cobalt hydroxide carbonate nanorods were calcined at 400 °C to fabricate pure cobaltic oxide (Co3O4) nanorods. Both nanorods were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetry (TG), infrared (IR) and temperature-programmed reduction (TPR). The catalytic activity towards the degradation of phenol over Co3O4 nanorods was further studied under continuous bubbling of air through the liquid phase. The results showed that phenol was degraded into harmless products (CO2 and malonic acid). The mechanism of phenol degradation was also discussed.

原文English
頁(從 - 到)105-110
頁數6
期刊Catalysis Today
131
發行號1-4
DOIs
出版狀態Published - 2008 二月 29

All Science Journal Classification (ASJC) codes

  • Catalysis
  • Chemistry(all)

指紋 深入研究「Microwave-assisted rapid fabrication of Co<sub>3</sub>O<sub>4</sub> nanorods and application to the degradation of phenol」主題。共同形成了獨特的指紋。

  • 引用此