Lifetime prognosis of lithium-ion batteries through novel accelerated degradation measurements and a combined gamma process and Monte Carlo method

Yu Chang Lin, Kuan Jung Chung

研究成果: Article

1 引文 斯高帕斯(Scopus)

摘要

A compositional prognostic-based assessment using the gamma process and Monte Carlo simulation was implemented to monitor the likelihood values of test Lithium-ion batteries on the failure threshold associated with capacity loss. The evaluation of capacity loss for the test LiFePO4 batteries using a novel dual dynamic stress accelerated degradation test, called D 2 SADT, to simulate a situation when driving an electric vehicle in the city. The Norris and Landzberg reliability model was applied to estimate activation energy of the test batteries. The test results show that the battery capacity always decreased at each measurement time-step during D2SADT to enable the novel test method. The variation of the activation energies for the test batteries indicate that the capacity loss of the test battery operated under certain power and temperature cycling conditions, which can be accelerated when the charge-discharge cycles increase. Moreover, the modeling results show that the gamma process combined with Monte Carlo simulations provides superior accuracy for predicting the lifetimes of the test batteries compared with the baseline lifetime data (i.e., real degradation route and lifetimes). The results presented high prediction quality for the proposed model as the error rates were within 5% and were obtained for all test batteries after a certain quantity of capacity loss, and remained so for at least three predictions.

原文English
文章編號559
期刊Applied Sciences (Switzerland)
9
發行號3
DOIs
出版狀態Published - 2019 二月 8

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Instrumentation
  • Engineering(all)
  • Process Chemistry and Technology
  • Computer Science Applications
  • Fluid Flow and Transfer Processes

指紋 深入研究「Lifetime prognosis of lithium-ion batteries through novel accelerated degradation measurements and a combined gamma process and Monte Carlo method」主題。共同形成了獨特的指紋。

  • 引用此