Laser scribing of indium tin oxide (ITO) thin films deposited on various substrates for touch panels

Shih Feng Tseng, Wen Tse Hsiao, Kuo Cheng Huang, Donyau Chiang, Ming-Fei Chen, Chang Pin Chou

研究成果: Article

76 引文 斯高帕斯(Scopus)

摘要

In this study, a Nd:YAG laser with wavelength of 1064 nm is used to scribe the indium tin oxide (ITO) thin films coated on three types of substrate materials, i.e. soda-lime glass, polycarbonate (PC), and cyclic-olefin-copolymer (COC) materials with thickness of 20 nm, 30 nm, and 20 nm, respectively. The effect of exposure time adjusted from 10 μs to 100 μs on the ablated mark width, depth, and electrical properties of the scribed film was investigated. The maximum laser power of 2.2 W was used to scribe these thin films. In addition, the surface morphology, surface reaction, surface roughness, optical properties, and electrical conductivity properties were measured by a scanning electron microscope, a three-dimensional confocal laser scanning microscope, an atomic force microscope, and a four-point probe. The measured results of surface morphology show that the residual ITO layer was produced on the scribed path with the laser exposure time at 10 μs and 20 μs. The better edge qualities of the scribed lines can be obtained when the exposure time extends from 30 μs to 60 μs. When the laser exposure time is longer than 60 μs, the partially burned areas of the scribed thin films on PC and COC substrates are observed. Moreover, the isolated line width and resistivity values increase when the laser exposure time increases. Crown

原文English
頁(從 - 到)1487-1494
頁數8
期刊Applied Surface Science
257
發行號5
DOIs
出版狀態Published - 2010 十二月 15

    指紋

All Science Journal Classification (ASJC) codes

  • Surfaces, Coatings and Films

引用此