Influence of Fe doping on the optical and magnetic characteristics of RTA treated transparent zn1-xFexO nanocrystalline films

Teng Tsai Lin, San Lin Young, Chung Yuan Kung, Hone Zern Chen, Ming Cheng Kao, Lance Horng, Teen Hang Meen

研究成果: Conference article同行評審

摘要

Herein transparent Zn1-xFexO nanocrystalline films have been prepared on glass substrates by sol-gel method followed by rapid thermal annealing treatment. The effecs of Fe doping on the microstructure, transmittance and magnetism of Zn1-xFexO nanocrys-talline films are investigated. The x-ray diffraction patterns of all compositions show the same wurtzite hexagonal structure with the space group P63/mc. FE-SEM images show uniform spherical grains of all Zn1-x Fe xO nanocrystalline films in which the grain size decreases progressively from 38.85 nm (x = 0.00) to 15.35 nm (x = 0.04). Red shift of the absorption edges is obtained from the optical transmittance spectra from 372 nm of undoped ZnO film to 367 nm of Zn0.96Fe0.04O film. The corresponding wide band gap energy of undoped ZnO film is 3.2986 eV which decreases slightly by 0.0191 eV of Zn0.96Fe 0.04O film. The saturation magnetization increases with the increase of Fe concentration. All Fe-doped ZnO films exhibit feromagnetic hysteresis curves which can be well fitted by the law of approaching to saturation with the formula, M = M S (1 - a/Hm).

原文English
頁(從 - 到)71-76
頁數6
期刊Integrated Ferroelectrics
143
發行號1
DOIs
出版狀態Published - 2013 七月 16
事件International Conference on Information, Communication and Engineering 2012, ICICE 2012 - Fuzhou, China
持續時間: 2012 十二月 152012 十二月 20

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Control and Systems Engineering
  • Ceramics and Composites
  • Condensed Matter Physics
  • Electrical and Electronic Engineering
  • Materials Chemistry

指紋 深入研究「Influence of Fe doping on the optical and magnetic characteristics of RTA treated transparent zn<sub>1-x</sub>Fe<sub>x</sub>O nanocrystalline films」主題。共同形成了獨特的指紋。

引用此