Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy

D. C. Chen, C. S. You

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

True stress-strain values were obtained from the tensile tests of 7075 aluminum alloy and finite element analysis. The results revealed that different ductile fracture criteria resulted in different accuracy of analysis. Moreover, factors affecting ductile fracture, such as effective stress, effective strain, and damage were analyzed. The maximum damage level occurred in the center, with its value reaching 0.454. The break happened in 12.9 s in the P1 point. In the P3 point, fracture was not revealed. It can be seen that the maximum damage was observed over the fracture area in the P1 point. Finite element analysis as applied to the 7075 aluminum alloy fracture criteria can be used for forging, drawing, and stamping of the materials.

原文English
頁(從 - 到)122-127
頁數6
期刊Strength of Materials
47
發行號1
DOIs
出版狀態Published - 2015 一月 1

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials

指紋 深入研究「Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy」主題。共同形成了獨特的指紋。

引用此