Exchange bias in NiFe/IrMn/CoFeB antidot arrays

Chao Hsien Huang, Sheng Yu Lo, Tian Chiuan Wu, Jong Ching Wu, Lance Horng

研究成果: Article同行評審

摘要

A study was made of the exchange bias effect in a structure of SiO 2/Ta (5 nm)/NiFe (7 nm)/IrMn (10 nm)/CoFeB (7 nm)/Ta (5 nm) with nanoscale antidot arrays. The nanostructure comprised rhomboid lattice antidot arrays with antidot diameters from 150 to 300 nm and a rhomboid lattice period of 500 nm. Enhancements of exchange bias HEX and coercivity H C were observed in the nanostructure antidot arrays compared to continuous film. These effects were mainly ascribed to the physical limitations on ferromagnetic and antiferromagnetic layers due to the presence of antidots. In antidot arrays, due to the presence of nonmagnetic holes, the ferromagnetic-ferromagnetic interactions in FM layer are reduced, leading to smaller ferromagnetic domains and larger exchange bias with the random-field model. In this paper, the relation between the antidot diameter size and exchange bias was studied.

原文English
文章編號6027667
頁(從 - 到)3494-3496
頁數3
期刊IEEE Transactions on Magnetics
47
發行號10
DOIs
出版狀態Published - 2011 十月 1

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Electrical and Electronic Engineering

指紋 深入研究「Exchange bias in NiFe/IrMn/CoFeB antidot arrays」主題。共同形成了獨特的指紋。

引用此