Dislocation reduction in GaN grown on stripe patterned r -plane sapphire substrates

Hou Guang Chen, Tsung Shine Ko, Shih Chun Ling, Tien Chang Lu, Hao Chung Kuo, Shing Chung Wang, Yue Han Wu, Li Chang

研究成果: Article

29 引文 (Scopus)

摘要

Extended defect reduction in GaN can be achieved via direct growth on stripe patterned (1 1- 02) r -plane sapphire substrates by metal organic chemical vapor deposition. The striped mesa is along [11 2- 0] with two etched sides in {0001} and {1 1- 01} faces. GaN grown on both etched facets in epitaxy exhibit different crystallographic relationships with sapphire substrate which are (1 1- 02)sapphire ∥ (11 2- 0)GaN and [11 2- 0]sapphire ∥ [1- 100]GaN, and (0001)sapphire ∥ (0001)GaN and [11 2- 0]sapphire ∥ [1- 100]GaN, respectively. The dislocation densities can be significantly reduced through epitaxial growth on the inclined lateral faces of mesas. Dislocation density in the order of ∼ 107 cm-2 can be achieved in the tilted GaN.

原文English
文章編號021914
期刊Applied Physics Letters
91
發行號2
DOIs
出版狀態Published - 2007 八月 1

指紋

sapphire
mesas
epitaxy
metalorganic chemical vapor deposition
flat surfaces
defects

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy (miscellaneous)

引用此文

Chen, H. G., Ko, T. S., Ling, S. C., Lu, T. C., Kuo, H. C., Wang, S. C., ... Chang, L. (2007). Dislocation reduction in GaN grown on stripe patterned r -plane sapphire substrates. Applied Physics Letters, 91(2), [021914]. https://doi.org/10.1063/1.2754643
Chen, Hou Guang ; Ko, Tsung Shine ; Ling, Shih Chun ; Lu, Tien Chang ; Kuo, Hao Chung ; Wang, Shing Chung ; Wu, Yue Han ; Chang, Li. / Dislocation reduction in GaN grown on stripe patterned r -plane sapphire substrates. 於: Applied Physics Letters. 2007 ; 卷 91, 編號 2.
@article{04aa9f7277f8458b95ffce29f937bb26,
title = "Dislocation reduction in GaN grown on stripe patterned r -plane sapphire substrates",
abstract = "Extended defect reduction in GaN can be achieved via direct growth on stripe patterned (1 1- 02) r -plane sapphire substrates by metal organic chemical vapor deposition. The striped mesa is along [11 2- 0] with two etched sides in {0001} and {1 1- 01} faces. GaN grown on both etched facets in epitaxy exhibit different crystallographic relationships with sapphire substrate which are (1 1- 02)sapphire ∥ (11 2- 0)GaN and [11 2- 0]sapphire ∥ [1- 100]GaN, and (0001)sapphire ∥ (0001)GaN and [11 2- 0]sapphire ∥ [1- 100]GaN, respectively. The dislocation densities can be significantly reduced through epitaxial growth on the inclined lateral faces of mesas. Dislocation density in the order of ∼ 107 cm-2 can be achieved in the tilted GaN.",
author = "Chen, {Hou Guang} and Ko, {Tsung Shine} and Ling, {Shih Chun} and Lu, {Tien Chang} and Kuo, {Hao Chung} and Wang, {Shing Chung} and Wu, {Yue Han} and Li Chang",
year = "2007",
month = "8",
day = "1",
doi = "10.1063/1.2754643",
language = "English",
volume = "91",
journal = "Applied Physics Letters",
issn = "0003-6951",
publisher = "American Institute of Physics Publising LLC",
number = "2",

}

Chen, HG, Ko, TS, Ling, SC, Lu, TC, Kuo, HC, Wang, SC, Wu, YH & Chang, L 2007, 'Dislocation reduction in GaN grown on stripe patterned r -plane sapphire substrates', Applied Physics Letters, 卷 91, 編號 2, 021914. https://doi.org/10.1063/1.2754643

Dislocation reduction in GaN grown on stripe patterned r -plane sapphire substrates. / Chen, Hou Guang; Ko, Tsung Shine; Ling, Shih Chun; Lu, Tien Chang; Kuo, Hao Chung; Wang, Shing Chung; Wu, Yue Han; Chang, Li.

於: Applied Physics Letters, 卷 91, 編號 2, 021914, 01.08.2007.

研究成果: Article

TY - JOUR

T1 - Dislocation reduction in GaN grown on stripe patterned r -plane sapphire substrates

AU - Chen, Hou Guang

AU - Ko, Tsung Shine

AU - Ling, Shih Chun

AU - Lu, Tien Chang

AU - Kuo, Hao Chung

AU - Wang, Shing Chung

AU - Wu, Yue Han

AU - Chang, Li

PY - 2007/8/1

Y1 - 2007/8/1

N2 - Extended defect reduction in GaN can be achieved via direct growth on stripe patterned (1 1- 02) r -plane sapphire substrates by metal organic chemical vapor deposition. The striped mesa is along [11 2- 0] with two etched sides in {0001} and {1 1- 01} faces. GaN grown on both etched facets in epitaxy exhibit different crystallographic relationships with sapphire substrate which are (1 1- 02)sapphire ∥ (11 2- 0)GaN and [11 2- 0]sapphire ∥ [1- 100]GaN, and (0001)sapphire ∥ (0001)GaN and [11 2- 0]sapphire ∥ [1- 100]GaN, respectively. The dislocation densities can be significantly reduced through epitaxial growth on the inclined lateral faces of mesas. Dislocation density in the order of ∼ 107 cm-2 can be achieved in the tilted GaN.

AB - Extended defect reduction in GaN can be achieved via direct growth on stripe patterned (1 1- 02) r -plane sapphire substrates by metal organic chemical vapor deposition. The striped mesa is along [11 2- 0] with two etched sides in {0001} and {1 1- 01} faces. GaN grown on both etched facets in epitaxy exhibit different crystallographic relationships with sapphire substrate which are (1 1- 02)sapphire ∥ (11 2- 0)GaN and [11 2- 0]sapphire ∥ [1- 100]GaN, and (0001)sapphire ∥ (0001)GaN and [11 2- 0]sapphire ∥ [1- 100]GaN, respectively. The dislocation densities can be significantly reduced through epitaxial growth on the inclined lateral faces of mesas. Dislocation density in the order of ∼ 107 cm-2 can be achieved in the tilted GaN.

UR - http://www.scopus.com/inward/record.url?scp=34547213277&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=34547213277&partnerID=8YFLogxK

U2 - 10.1063/1.2754643

DO - 10.1063/1.2754643

M3 - Article

AN - SCOPUS:34547213277

VL - 91

JO - Applied Physics Letters

JF - Applied Physics Letters

SN - 0003-6951

IS - 2

M1 - 021914

ER -