Characterizing the electrical and optical properties of AZO/AgPd/AZO multilayer film using RF magnetron sputtering

Yi-Cheng or Y. C. Lin, Kun Hsin Lu, Jhih Jhong Chen

研究成果: Article同行評審

3 引文 斯高帕斯(Scopus)

摘要

In this study, radio frequency (RF) magnetron sputtering was used to investigate the effects of process parameters on the electrical and optical properties of AZO(ZnO:Al) and AgPd multilayer films on type 1737F Corning glass. Experiments were performed using RF power and working pressure as variable parameters. The best transmittance (90%) and lowest resistivity (8.28 ×10-4 Ωcm) were obtained from multilayer films of AZO/AgPd/AZO, in which the AgPd was deposited using RF power of 150 W without substrate heating to thicknesses of AZO(50 nm)/AgPd(5 nm)/AZO(50 nm). An increase in working pressure led to an increase in resistivity and a decrease in transmittance, due to an increase in the number of defects in the AgPd layer, which produced a discontinuous interface between the AgPd and AZO. The relationship between transmittance/resistance and RF power is non-linear. The inner AgPd metal layer largely determines the optical quality and electrical resistivity of AZO/AgPd/AZO multilayer films.

原文English
頁(從 - 到)475-482
頁數8
期刊Chinese Journal of Physics
54
發行號4
DOIs
出版狀態Published - 2016 一月 1

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

指紋 深入研究「Characterizing the electrical and optical properties of AZO/AgPd/AZO multilayer film using RF magnetron sputtering」主題。共同形成了獨特的指紋。

引用此