Brief rapid thermal treatment effect on patterned CoFeB-based magnetic tunneling junctions

Kuo Ming Wu, Chao Hsien Huang, Yung Hung Wang, Ming Jer Kao, Ming Jinn Tsai, Jong Ching Wu, Lance Horng

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

The brief thermal treatment effects on the magnetoresistance of microstructured Co60 Fe20 B20 -based magnetic tunneling junctions have been studied. The elliptical shape of devices with long/short axis of 42 μm was patterned out of film stack of seed layer (20) PtMn (15) Co60 Fe20 B20 (3) Al (0.7) oxide C60 Fe20 B20 (20) capping layer (48) (thickness unit in nanometers) combining conventional lithography and inductively coupled plasma reactive ion beam etching technologies. The thermal annealing was carried out with device loading into a furnace with preset temperatures ranging from 100 to 400 °C for only 5 min in the absence of any external magnetic field. The magnetoresistance was found to increase with increasing annealing temperatures up to 250 °C and then decrease at higher annealing temperatures. In addition, the magnetoresistance ratio of around 35%, similar to that of as-fabricated devices, sustains up to annealing temperature of 350 °C. This survival of magnetoresistance at higher annealing temperature is due to boron conservation in the amorphous CoFeB ferromagnetic layer at higher annealing temperature for only a short time, which is manifested using x-ray diffractometer technique.

原文English
文章編號09B503
期刊Journal of Applied Physics
101
發行號9
DOIs
出版狀態Published - 2007 五月 21

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

指紋 深入研究「Brief rapid thermal treatment effect on patterned CoFeB-based magnetic tunneling junctions」主題。共同形成了獨特的指紋。

引用此