Irreversibility lines of HgBa2CuO4+δ with different oxygen contents

R. Usami, H. Kubota, R. Puzniak, Chia-Jyi Liu, H. Yamauchi

Research output: Contribution to journalArticlepeer-review

2 Citations (Scopus)


Single phase HgBa2CuO4+δ samples were annealed in flowing oxygen gas or in flowing argon gas. Oxygen contents of both samples determined by iodometric titrations indicate that the samples annealed in oxygen gas and in argon gas were respectively in over-doped and in under-doped region. Both samples were respectively grain-aligned in magnetic fields. Hysteresis loops for grain-aligned over-doped and under-doped samples were measured in applied fields parallel and perpendicular to the c-axis. Region where irreversibility lines of over-doped sample was located was found to be higher than that of under-doped sample. Irreversibility line of over-doped sample was found to be higher than that of YBa2Cu3O6.6. Anisotropy of irreversibility lines of both samples were found to be smaller than that of Y-123 superconductors.

Original languageEnglish
Pages (from-to)2759-2760
Number of pages2
JournalPhysica C: Superconductivity and its applications
Issue numberPART 4
Publication statusPublished - 1994 Jan 1

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Energy Engineering and Power Technology
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Irreversibility lines of HgBa<sub>2</sub>CuO<sub>4+δ</sub> with different oxygen contents'. Together they form a unique fingerprint.

Cite this